1 6587 steel equivalent to 17cr2ni2mo steel
Brands: Shanghai Katalor
Transport: By bulk or Containers;
Supply ability : 3000 metric tons/ month;
Payment terms : L/C, T/T;
Katalor have 1 6587 steel equivalent to 17cr2ni2mo steel suppliers and manufacturer ,if you need 1 6587 steel equivalent to 17cr2ni2mo steel price and specification ,please contact us.
1 6587 steel equivalent to 17cr2ni2mo steel
1 6587 steel equivalent to 17cr2ni2mo steel 18CrNiMo7-6 / 1.6587 Alloy special steel - equivalent ...
Chemical composition % of steel 18CrNiMo7-6 (1.6587): EN 10084-2008 Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser, other than for the purpose of finishing the heat.
1 6587 steel equivalent to 17cr2ni2mo steel 17Cr2Ni2Mo (GB ) - Worldwide equivalent grades - Steel …
Chemical composition and properties of european equivalents (EN) for 17Cr2Ni2Mo (China, GB ): 18CrNiMo7-6 (1.6587) , 17Cr2Ni2Mo (China, GB ) - European (EU, EN) and wordwide Steel equivalent grades. These comparison table is only intended as an indication of the closest khown equivalent …
1 6587 steel equivalent to 17cr2ni2mo steel DIN 1.6587 (18CrNiMo7-6) NICKEL-MOLYBDENUM …
DIN 1.6587 (18CrNiMo7-6) NICKEL-MOLYBDENUM ALLOY STEEL NEAREST EQUIVALENT DIN 18CrNiMo7-6 AISI 4820 JIS - CHARACTERISTIC Nickel- Molybdenum Alloy Steel for case hardening steel use in area of heavy and high strained gear parts
1 6587 steel equivalent to 17cr2ni2mo steel 1.6587 Steel - Special Steel
Alloy steel is steel alloyed with a variety of elements in total amounts of between 1.0% and 50% by weight to improve its mechanical properties. Alloy steels are broken down into two groups: low alloy steels and high alloy steels.
1 6587 steel equivalent to 17cr2ni2mo steel 18CrNiMo7-6, 1.6587, 18NiCrMo5 - case-hardening steel
17HNM, 18NiCrMo5, 17CrNiMo6-4, 18CrNiMo7-6, 1.6566 - specification and application. Alloy steel 17HNM is a grade consisting of the addition of chromium, nickel, molybdenum and coal with a range characteristic for all carburizing grades. 17HNM materials, unlike other simple steel grades, can be used for much larger sizes and loads.
1 6587 steel equivalent to 17cr2ni2mo steel 4317/17CrNiMo6 17Cr2Ni2Mo Alloy Steel - …
4317/17CrNiMo6 17Cr2Ni2Mo Alloy Steel The 17CrNiMo6 is the standard steel number of DIN 17210 - (86) in Germany, and the European standard is 18crnimo7-6, which corresponds to the 17Cr2Ni2Mo of GB 17Cr2Ni2Mo is not a GB material, but a JB material.The specific standard number is: JB/T 6395-2010 large gear, tooth ring forging
1 6587 steel equivalent to 17cr2ni2mo steel CASE HARDENING STEEL 18CrNiMo7- 6 or 17CrNiMo6
CASE HARDENING STEEL–18CrNiMo7- 6 or 17CrNiMo6. 8CrNiMo7- 6 Chrome-Nickel-Moly Carburising Steel generally supplied annealed to HB 229max. Carburised and heat treated it develops a hard wear resistant case to HRC 60-63 and a tough strong core with a typical tensile strength range of 900-1300 MPa, in small to fairly large sections.
1 6587 steel equivalent to 17cr2ni2mo steel 17CrNiMo6 steel - steel-grades.com
Stainless Steel, Special Steel, Compressor Blading, Turbine Blading, Superalloy Supplier. 17CrNiMo6 can be supplied as steel plate/ sheet, round steel bar, steel tube/pipe, steel stripe, steel billet, steel ingot, steel wire rods. electroslag, forged ring/ block,etc.
1 6587 steel equivalent to 17cr2ni2mo steel 1.6582 / 34CrNiMo6 Steel - Alloy Engineering Steel | Steel Bar
DIN 1.6582 / 34CrNiMo6 Steel is an important alloy engineering steel grade as per DIN Germany standard. It has high strength,high toughness and good hardenability. DIN 1.6582 steel has the stability of resistance to overheating,but the white sensitivity of 34CrNiMo6 is high. It also has the temper brittleness,so the weldability is poor.
1 6587 steel equivalent to 17cr2ni2mo steel Atlas 6587 Case Hardening Alloy Steel Bar 6587
Atlas 6587. Revised April 2006 2 of 3. Atlas Specialty Metals Case Hardening Alloy Steel Bar 6587. The minimum tempering time is 1 hour, but a tempering period of 1 hour per 25mm of section is recommended. If the steel is to be direct hardened, then in general, a carburizing temperature of 950°C is not to be exceeded.
- sa387 gr12cl2 steel mill
- aisi 201 202 304 316l 430 cold rolled stainless sheet
- stainless steel rope chain for men
- 80x160 erw welded s q rectangular steel tubes
- cold rolled 304 316l 2b stainless steel plates
- prime quality corten b steel
- kr grade f36 angle steel
- astm a269 789 790 seamless and welded stainless steel plate
- en s355jrh building structures erw steel
- nve cold carbon steel